铜材材质：紫铜类（纯铜）T2.C1100.C11000;无氧铜TU1.C1020.C10200;加磷脱氧铜TP2.C1220.C12200;H96.C2100.C21000.H90.C2200.C22000.H85.C2300.C23000.H80.C2400.C24000.H68A. C2680. C26200.H65.C2700.C26800.H62.C2720.C27400.H59;铅黄铜HPb59-1.C3710.C37800.HPb59-2.C3771.C35300.HPb60-2.C3604.C36000.HPb63-3.C3560.C34500.HPb63-0.1.C34900;C5210.C52100.C5191.C5240.C5100;铍铜C17200.C17500.C17000;铝黄铜HAi77-2.C6870.C68700. HAi60-1-1.C6782.C67000.HAi59-3-2.C67800.HAi66-6-3-2.C6872;锡黄铜HSn62-1.HSn70-1AB;锰黄铜 HMn58-2.C67400.HMn57-3-1;铁黄铜HFe59-1-1.C6782.C67820;硅黄铜HSi80-3.C69400;青铜类：锡青铜 QSn4-3,QSn6.5-0.1.QSn7-0.2.C5212.C52100.QSn6.5-0.4;QAi9-2.C61000.QAi9-4.QAi10-3-1.5. C6161.C61900.QAi10--4-4.C6301.C63000.C63200;QSi3-1.C65500.C65800.QSi1-3.C64700.QSi1.8;QMn5;锆青QZr0.2-0.4;铬锆铜Cr0.5.C18100.C18200.C18400.QCr1-2.QCr1-0.15.C18150;镉青铜QCd1.0；铍青铜QBe1.8.QBe2.0；白铜类：B19.B25；铁白铜BFe10-1--1.B111.C70600.BFe30--1-1.B111. C71500；锰白铜BMn3-12.BMn40-1.5；锌白铜BZn15-20；铝白铜BAi13-3；镍及合金：N6.NCu40-2-1. NCu28-2.5-1.5 7。我们的承诺』服务三保：保证质量、保证时间、保证数量 服务宗旨：雄厚的实力、优质的产品、低廉的价格、 的服务。经营原则：顾客至上、质量优良、品种齐全、价格合理。经营理念：以完美的品质开拓市场、以诚心经营赢得客户！郑重承诺：保证以 的产品、 的质量、 的价格、完善的服务来答谢新老顾客的信赖. 郑重提示产品质量保证，如出现质量问题，按百倍赔款！！！

天津阔恒兴旺国际贸易有限公司根据铜合金铸锭的特点，自由锻的注意事项有：（1）铜合金的锻造温度范围较窄，为避免在锻造过程中坯料温度迅速下降而落入脆性区，在锻造前应将锤头、砧面以及操作工具如冲头、芯轴、胎模、漏盘等预热至200℃以上。操作时动作应轻快，坯料在砧面上要经常翻动。进行冲孔时，冲头应预热至尽可能高的温度，使与冲头接触的金属温度下降不致太多，避免孔的边缘产生裂纹。锻造时如坯料温度下降至脆性区范围，应立即停锻，重新加热后再恢复锻造。（2）铜合金质地较软，在拔长时压出的棱角比较尖锐，为避免产生折叠缺陷，锻造铜合金的砧块的棱边应倒圆R10以上，操作时送进量与压下量之比应适当加大，可保持在0.7～1.0，同时锤击时应尽可能快一些。在锻制带孔法兰时，如果先冲孔，再在胎模内镦粗头部，容易在孔的内壁产生折叠缺陷，因此，锻造铜合金带孔法兰时，一般应先在胎模中镦粗头部， 再冲孔；也可在冲孔后，在坯料孔中放置芯棒再在胎模中镦粗成形头部。（3）黄铜对内应力比较敏感，内应力较大时容易自行开裂。锻制长轴类黄铜锻件时，应反复掉头锻造，并均匀翻动锻件，使锻件各段的变形温度相差不致过大，以便降低锻件的内应力并获得比较均匀的组织。